Organic electroluminescent materials and devices

ABSTRACT

A new class of compounds containing aza-dibenzothiophene or aza-dibenzofuran are provided. The compounds may be used in organic light emitting devices giving improved stability, improved efficiency, long lifetime and low operational voltage. In particular, the compounds may be used as the host material of an emissive layer having a host and an emissive dopant, or as a material in an enhancement layer.

This application claims priority to U.S. Provisional Application No. 61/145,370, filed Jan. 16, 2009, the disclosure of which is herein expressly incorporated by reference in its entirety. This application is related to U.S. application Ser. No. 12/209,928, filed Sep. 12, 2008, and U.S. application Ser. No. 11/443,586, filed May 31, 2006.

The claimed invention was made by, on behalf of, and/or in connection with one or more of the following parties to a joint university corporation research agreement: Regents of the University of Michigan, Princeton University, The University of Southern California, and the Universal Display Corporation. The agreement was in effect on and before the date the claimed invention was made, and the claimed invention was made as a result of activities undertaken within the scope of the agreement.

FIELD OF THE INVENTION

The present invention relates to novel organic complexes containing aza-dibenzothiophene or aza-dibenzofuran. The materials may be useful in organic light emitting devices (OLEDs).

BACKGROUND

Opto-electronic devices that make use of organic materials are becoming increasingly desirable for a number of reasons. Many of the materials used to make such devices are relatively inexpensive, so organic opto-electronic devices have the potential for cost advantages over inorganic devices. In addition, the inherent properties of organic materials, such as their flexibility, may make them well suited for particular applications such as fabrication on a flexible substrate. Examples of organic opto-electronic devices include organic light emitting devices (OLEDs), organic phototransistors, organic photovoltaic cells, and organic photodetectors. For OLEDs, the organic materials may have performance advantages over conventional materials. For example, the wavelength at which an organic emissive layer emits light may generally be readily tuned with appropriate dopants.

OLEDs make use of thin organic films that emit light when voltage is applied across the device. OLEDs are becoming an increasingly interesting technology for use in applications such as flat panel displays, illumination, and backlighting. Several OLED materials and configurations are described in U.S. Pat. Nos. 5,844,363, 6,303,238, and 5,707,745, which are incorporated herein by reference in their entirety.

One application for phosphorescent emissive molecules is a full color display. Industry standards for such a display call for pixels adapted to emit particular colors, referred to as “saturated” colors. In particular, these standards call for saturated red, green, and blue pixels. Color may be measured using CIE coordinates, which are well known to the art.

One example of a green emissive molecule is tris(2-phenylpyridine) iridium, denoted Ir(ppy)₃, which has the structure:

In this, and later figures herein, we depict the dative bond from nitrogen to metal (here, Ir) as a straight line.

As used herein, the term “organic” includes polymeric materials as well as small molecule organic materials that may be used to fabricate organic opto-electronic devices. “Small molecule” refers to any organic material that is not a polymer, and “small molecules” may actually be quite large. Small molecules may include repeat units in some circumstances. For example, using a long chain alkyl group as a substituent does not remove a molecule from the “small molecule” class. Small molecules may also be incorporated into polymers, for example as a pendent group on a polymer backbone or as a part of the backbone. Small molecules may also serve as the core moiety of a dendrimer, which consists of a series of chemical shells built on the core moiety. The core moiety of a dendrimer may be a fluorescent or phosphorescent small molecule emitter. A dendrimer may be a “small molecule,” and it is believed that all dendrimers currently used in the field of OLEDs are small molecules.

As used herein, “top” means furthest away from the substrate, while “bottom” means closest to the substrate. Where a first layer is described as “disposed over” a second layer, the first layer is disposed further away from substrate. There may be other layers between the first and second layer, unless it is specified that the first layer is “in contact with” the second layer. For example, a cathode may be described as “disposed over” an anode, even though there are various organic layers in between.

As used herein, “solution processible” means capable of being dissolved, dispersed, or transported in and/or deposited from a liquid medium, either in solution or suspension form.

A ligand may be referred to as “photoactive” when it is believed that the ligand directly contributes to the photoactive properties of an emissive material. A ligand may be referred to as “ancillary” when it is believed that the ligand does not contribute to the photoactive properties of an emissive material, although an ancillary ligand may alter the properties of a photoactive ligand.

As used herein, and as would be generally understood by one skilled in the art, a first “Highest Occupied Molecular Orbital” (HOMO) or “Lowest Unoccupied Molecular Orbital” (LUMO) energy level is “greater than” or “higher than” a second HOMO or LUMO energy level if the first energy level is closer to the vacuum energy level. Since ionization potentials (IP) are measured as a negative energy relative to a vacuum level, a higher HOMO energy level corresponds to an IP having a smaller absolute value (an IP that is less negative). Similarly, a higher LUMO energy level corresponds to an electron affinity (EA) having a smaller absolute value (an EA that is less negative). On a conventional energy level diagram, with the vacuum level at the top, the LUMO energy level of a material is higher than the HOMO energy level of the same material. A “higher” HOMO or LUMO energy level appears closer to the top of such a diagram than a “lower” HOMO or LUMO energy level.

As used herein, and as would be generally understood by one skilled in the art, a first work function is “greater than” or “higher than” a second work function if the first work function has a higher absolute value. Because work functions are generally measured as negative numbers relative to vacuum level, this means that a “higher” work function is more negative. On a conventional energy level diagram, with the vacuum level at the top, a “higher” work function is illustrated as further away from the vacuum level in the downward direction. Thus, the definitions of HOMO and LUMO energy levels follow a different convention than work functions.

More details on OLEDs, and the definitions described above, can be found in U.S. Pat. No. 7,279,704, which is incorporated herein by reference in its entirety.

SUMMARY OF THE INVENTION

A process is provided for making aza-dibenzothiophene compounds or aza-dibenzofuran compounds. The process, comprising treating an acetic acid solution of an amino-arylthio pyridine intermediate having the formula

wherein one of X₁ and X₂ is nitrogen and the other of X₁ and X₂ is carbon and wherein Y is S or O, with ^(t)BuONO to produce an aza complex having the formula

R₁ and R₂ may represent mono, di, tri or tetra substitutions. R₁ is selected from the group consisting of hydrogen, alkyl, aryl, heteroaryl and halide. Preferably, R₁ is halide. R₂ is selected from the group consisting of hydrogen, alkyl, aryl and halide. Preferably, one of X₁ and X₂ may be carbon and the other may be nitrogen. More preferably, X₁ is nitrogen and X₂ is carbon or X₁ is carbon and X₂ is nitrogen. Preferably, Y is S. Alternatively, Y may preferably be O. R₂ may include at least one halide, and R₂ may include only halide substituents. The process may be used to make compounds where R₂ is not halide and the amino-arylthio pyridine intermediate is treated with H₂SO₄ prior to treatment with ^(t)BuONO. The yield of

may be greater than 50%.

A novel class of aza-dibenzothiophene and aza-dibenzofuran compounds are provided. The compounds have the formula:

X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom, and at least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom. Y is S or O. R₁ and R₂ may represent mono, di tri, or tetra substitutions. R₁ and R₂ are independently selected from the group consisting of hydrogen, alkyl, aryl and halide, and at least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ may represent mono, di, tri, tetra or penta substitutions, and R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, m and n are 0, 1, 2, 3, or 4; and wherein m+n is equal to or greater than 2 and m+n is equal to or less than 6. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Additionally, a novel class of aza-dibenzothiophene and aza-dibenzofuran compounds are provided. The compounds have the formula:

X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom, and at least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom. Y is S or O. R₁ and R₂ may represent mono, di, tri, or tetra substitutions. R₁ and R₂ are independently selected from the group consisting of hydrogen, alkyl, aryl and halide, and at least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ may represent mono, di, tri, tetra or penta substitutions, and R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, m and n are 0, 1, 2, 3, or 4; and wherein m+n is equal to or greater than 2 and m+n is equal to or less than 6. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Compounds are also provided where one of R₁ and R₂ is hydrogen and the other of R₁ and R₂ is selected from the groups consisting of

In addition, compounds are provided wherein both R₁ and R₂ are selected from the groups provided herein. Moreover, compounds are provided wherein R₁ is selected from the groups provided herein.

Specific examples of the aza-dibenzothiophene compounds and aza-dibenzofuran compounds are provided including Compounds 1-93.

Specific examples of the aza-dibenzothiophene compounds and aza-dibenzofuran compounds are provided including Compounds 1-79.

A first device comprising an organic light emitting device is provided. The device further comprises an anode, a cathode, and an organic layer disposed between the anode and the cathode. The organic layer comprises a compound having FORMULA I. In particular, the organic layer of the device may comprise a compound selected from Compounds 1-93.

In one aspect, the first device is a consumer product.

An organic light emitting device is also provided. The device comprises an anode, a cathode, and an organic layer disposed between the anode and the cathode. The organic layer comprises a compound having FORMULA I. In particular, the organic layer of the device may comprise a compound selected from Compound 1-79. Preferably, the organic layer is an emissive layer and the compound having FORMULA I is a host. The emissive layer may further comprise an emissive dopant. Preferably, the emissive dopant has the formula

where R₁ and R₂ are each independently selected from the group consisting of hydrogen, alkyl, and aryl.

Additionally, a consumer product is also provided. The product contains a device that has an anode, a cathode, and an organic layer disposed between the anode and the cathode, where the organic layer comprises a compounds having FORMULA I.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an organic light emitting device.

FIG. 2 shows an inverted organic light emitting device that does not have a separate electron transport layer.

FIG. 3 shows aza-dibenzothiophene compounds and aza-dibenzofuran compounds.

FIG. 4 shows reactions in synthetic pathways.

DETAILED DESCRIPTION

Generally, an OLED comprises at least one organic layer disposed between and electrically connected to an anode and a cathode. When a current is applied, the anode injects holes and the cathode injects electrons into the organic layer(s). The injected holes and electrons each migrate toward the oppositely charged electrode. When an electron and hole localize on the same molecule, an “exciton,” which is a localized electron-hole pair having an excited energy state, is formed. Light is emitted when the exciton relaxes via a photoemissive mechanism. In some cases, the exciton may be localized on an excimer or an exciplex. Non-radiative mechanisms, such as thermal relaxation, may also occur, but are generally considered undesirable.

The initial OLEDs used emissive molecules that emitted light from their singlet states (“fluorescence”) as disclosed, for example, in U.S. Pat. No. 4,769,292, which is incorporated by reference in its entirety. Fluorescent emission generally occurs in a time frame of less than 10 nanoseconds.

More recently, OLEDs having emissive materials that emit light from triplet states (“phosphorescence”) have been demonstrated. Baldo et al., “Highly Efficient Phosphorescent Emission from Organic Electroluminescent Devices,” Nature, vol. 395, 151-154, 1998; (“Baldo-I”) and Baldo et al., “Very high-efficiency green organic light-emitting devices based on electrophosphorescence,” Appl. Phys. Lett., vol. 75, No. 3, 4-6 (1999) (“Baldo-II”), which are incorporated by reference in their entireties. Phosphorescence is described in more detail in U.S. Pat. No. 7,279,704 at cols. 5-6, which are incorporated by reference.

FIG. 1 shows an organic light emitting device 100. The figures are not necessarily drawn to scale. Device 100 may include a substrate 110, an anode 115, a hole injection layer 120, a hole transport layer 125, an electron blocking layer 130, an emissive layer 135, a hole blocking layer 140, an electron transport layer 145, an electron injection layer 150, a protective layer 155, and a cathode 160. Cathode 160 is a compound cathode having a first conductive layer 162 and a second conductive layer 164. Device 100 may be fabricated by depositing the layers described, in order. The properties and functions of these various layers, as well as example materials, are described in more detail in U.S. Pat. No. 7,279,704 at cols. 6-10, which are incorporated by reference.

More examples for each of these layers are available. For example, a flexible and transparent substrate-anode combination is disclosed in U.S. Pat. No. 5,844,363, which is incorporated by reference in its entirety. An example of a p-doped hole transport layer is m-MTDATA doped with F.sub.4-TCNQ at a molar ratio of 50:1, as disclosed in U.S. Patent Application Publication No. 2003/0230980, which is incorporated by reference in its entirety. Examples of emissive and host materials are disclosed in U.S. Pat. No. 6,303,238 to Thompson et al., which is incorporated by reference in its entirety. An example of an n-doped electron transport layer is BPhen doped with Li at a molar ratio of 1:1, as disclosed in U.S. Patent Application Publication No. 2003/0230980, which is incorporated by reference in its entirety. U.S. Pat. Nos. 5,703,436 and 5,707,745, which are incorporated by reference in their entireties, disclose examples of cathodes including compound cathodes having a thin layer of metal such as Mg:Ag with an overlying transparent, electrically-conductive, sputter-deposited ITO layer. The theory and use of blocking layers is described in more detail in U.S. Pat. No. 6,097,147 and U.S. Patent Application Publication No. 2003/0230980, which are incorporated by reference in their entireties. Examples of injection layers are provided in U.S. Patent Application Publication No. 2004/0174116, which is incorporated by reference in its entirety. A description of protective layers may be found in U.S. Patent Application Publication No. 2004/0174116, which is incorporated by reference in its entirety.

FIG. 2 shows an inverted OLED 200. The device includes a substrate 210, a cathode 215, an emissive layer 220, a hole transport layer 225, and an anode 230. Device 200 may be fabricated by depositing the layers described, in order. Because the most common OLED configuration has a cathode disposed over the anode, and device 200 has cathode 215 disposed under anode 230, device 200 may be referred to as an “inverted” OLED. Materials similar to those described with respect to device 100 may be used in the corresponding layers of device 200. FIG. 2 provides one example of how some layers may be omitted from the structure of device 100.

The simple layered structure illustrated in FIGS. 1 and 2 is provided by way of non-limiting example, and it is understood that embodiments of the invention may be used in connection with a wide variety of other structures. The specific materials and structures described are exemplary in nature, and other materials and structures may be used. Functional OLEDs may be achieved by combining the various layers described in different ways, or layers may be omitted entirely, based on design, performance, and cost factors. Other layers not specifically described may also be included. Materials other than those specifically described may be used. Although many of the examples provided herein describe various layers as comprising a single material, it is understood that combinations of materials, such as a mixture of host and dopant, or more generally a mixture, may be used. Also, the layers may have various sublayers. The names given to the various layers herein are not intended to be strictly limiting. For example, in device 200, hole transport layer 225 transports holes and injects holes into emissive layer 220, and may be described as a hole transport layer or a hole injection layer. In one embodiment, an OLED may be described as having an “organic layer” disposed between a cathode and an anode. This organic layer may comprise a single layer, or may further comprise multiple layers of different organic materials as described, for example, with respect to FIGS. 1 and 2.

Structures and materials not specifically described may also be used, such as OLEDs comprised of polymeric materials (PLEDs) such as disclosed in U.S. Pat. No. 5,247,190 to Friend et al., which is incorporated by reference in its entirety. By way of further example, OLEDs having a single organic layer may be used. OLEDs may be stacked, for example as described in U.S. Pat. No. 5,707,745 to Forrest et al, which is incorporated by reference in its entirety. The OLED structure may deviate from the simple layered structure illustrated in FIGS. 1 and 2. For example, the substrate may include an angled reflective surface to improve out-coupling, such as a mesa structure as described in U.S. Pat. No. 6,091,195 to Forrest et al., and/or a pit structure as described in U.S. Pat. No. 5,834,893 to Bulovic et al., which are incorporated by reference in their entireties.

Unless otherwise specified, any of the layers of the various embodiments may be deposited by any suitable method. For the organic layers, preferred methods include thermal evaporation, ink-jet, such as described in U.S. Pat. Nos. 6,013,982 and 6,087,196, which are incorporated by reference in their entireties, organic vapor phase deposition (OVPD), such as described in U.S. Pat. No. 6,337,102 to Forrest et al., which is incorporated by reference in its entirety, and deposition by organic vapor jet printing (OVJP), such as described in U.S. patent application Ser. No. 10/233,470, which is incorporated by reference in its entirety. Other suitable deposition methods include spin coating and other solution based processes. Solution based processes are preferably carried out in nitrogen or an inert atmosphere. For the other layers, preferred methods include thermal evaporation. Preferred patterning methods include deposition through a mask, cold welding such as described in U.S. Pat. Nos. 6,294,398 and 6,468,819, which are incorporated by reference in their entireties, and patterning associated with some of the deposition methods such as ink-jet and OVJD. Other methods may also be used. The materials to be deposited may be modified to make them compatible with a particular deposition method. For example, substituents such as alkyl and aryl groups, branched or unbranched, and preferably containing at least 3 carbons, may be used in small molecules to enhance their ability to undergo solution processing. Substituents having 20 carbons or more may be used, and 3-20 carbons is a preferred range. Materials with asymmetric structures may have better solution processibility than those having symmetric structures, because asymmetric materials may have a lower tendency to recrystallize. Dendrimer substituents may be used to enhance the ability of small molecules to undergo solution processing.

Devices fabricated in accordance with embodiments of the invention may be incorporated into a wide variety of consumer products, including flat panel displays, computer monitors, televisions, billboards, lights for interior or exterior illumination and/or signaling, heads up displays, fully transparent displays, flexible displays, laser printers, telephones, cell phones, personal digital assistants (PDAs), laptop computers, digital cameras, camcorders, viewfinders, micro-displays, vehicles, a large area wall, theater or stadium screen, or a sign. Various control mechanisms may be used to control devices fabricated in accordance with the present invention, including passive matrix and active matrix. Many of the devices are intended for use in a temperature range comfortable to humans, such as 18 degrees C. to 30 degrees C., and more preferably at room temperature (20-25 degrees C.).

The materials and structures described herein may have applications in devices other than OLEDs. For example, other optoelectronic devices such as organic solar cells and organic photodetectors may employ the materials and structures. More generally, organic devices, such as organic transistors, may employ the materials and structures.

The terms halo, halogen, alkyl, cycloalkyl, alkenyl, alkynyl, arylkyl, heterocyclic group, aryl, aromatic group, and heteroaryl are known to the art, and are defined in U.S. Pat. No. 7,279,704 at cols. 31-32, which are incorporated herein by reference.

A new class of compounds containing an aza-dibenzothiophene or aza-dibenzofuran core are provided (illustrated in FIG. 3). In particular, aza-dibenzothiophene compounds or aza-dibenzofuran compounds further substituted with triphenylene and/or nitrogen-containing substituents are provided. These compounds may be advantageously used in phosphorescent organic light emitting devices. Preferably, these compounds may be used as a host material in an emissive layer or as a material in an enhancement layer.

While there are existing syntheses for aza-dibenzothiophene compounds and aza-dibenzofuran compounds, these synthetic routes may have limited practicality. For example, substrates of aza-dibenzothiophene and aza-dibenzofuran were first synthesized by the well-known Pschorr Cyclization method which involves the formation of diazonium salt followed by cyclization in an aqueous medium with or without catalysts, such as Cu, CuCl. However, the general yield of the Pschorr Cyclization method is not consistent and can be less than 10%. Therefore, it is highly desirable to provide a process for making aza-dibenzothiophene compounds and aza-dibenzofuran compounds in improved yields. A new process for making aza-dibenzothiophene compounds is provided herein (illustrated in FIG. 4). The processes described in this invention differ from the existing synthesis at least by using acetic acid, not aqueous medium, and do not employ any metal catalyst. Preferably, the acetic acid is pure (or glacial) acetic acid. The process provided herein may provide yields higher than 50% or yields higher than 70%.

Dibenzothiophene-containing and dibenzofuran-containing materials are typically hole transporting materials that have a relatively high triplet energy. Given the beneficial properties of dibenzothiophene and dibenzofuran, these compounds have been used in the OLED area and some of these compounds have achieved good device performance. See Lin et al., Dibenzothiophene-containing Materials in Phosphorescent Light Emitting Diodes, 2008, U.S. application Ser. No. 12/208,907 and Ma et al., Benzo-fused Thiophene/Triphenylene Hybrid Materials, 2008, PCT/US2008/072499. Without being bound by theory, it is thought that anion injection and anion stability may play an important role in device stability. In order to have high anion stability and a lower energy barrier for anion injection to the emissive layer, compounds with a lower LUMO level are desired. In particular, dibenzothiophene and dibenzofuran containing compounds having a lower LUMO value (i.e., compounds that are more easily reduced) may be beneficial.

The compounds provided herein contain an aza-dibenzothiophene or aza-dibenzofuran core further substituted with particular chemical groups having desirable properties. Specifically, these aza-type compounds are substituted with triphenylene groups and/or nitrogen-containing groups (e.g., carbazole) to maintain high triplet energy and provide improved charge transport properties. Therefore, these substituted aza-dibenzothiophene compounds and aza-dibenzofuran compounds may provide devices having improved stability, improved efficiency, and a longer lifetime. In addition, these aza-type compounds have been demonstrated to be more easily reduced than their dibenzothiophene or dibenzofuran counterparts, and thus may provide devices having low operating voltage.

Triphenylene is a polyaromatic hydrocarbon with high triplet energy, yet high π-conjugation and a relatively small energy difference between the first singlet and first triplet levels. This would indicate that triphenylene has relatively easily accessible HOMO and LUMO levels compared to other aromatic compounds with similar triplet energy (e.g., biphenyl). These characteristics of triphenylene make it a good molecular building block in OLED hosts to stabilize charges (hole or electron). One advantage of using triphenylene and its derivatives as hosts is that it can accommodate red, green and even blue phosphorescent dopants to give high efficiency without energy quenching. Triphenylene hosts may be used to provide high efficiency and stability PHOLEDs. See Kwong and Alleyene, Triphenylene Hosts in Phosphorescent Light Emitting Diodes, 2006, 60 pp, U.S. 2006/0280965 A1. A compound containing an aza-dibenzothiophene or aza-dibenzofuran core and a triphenylene moiety may be beneficial as a host in PHOLEDs. More specifically, the triplet energy of both portions of the compound are relatively high thereby maintaining an overall high triplet energy. In addition, the combination of these two groups in one compound may also offer improved charge balance thus improving device efficiency and lifetime. Non-limiting examples triphenylene groups that may be the triphenylene moiety of such compounds may include

Nitrogen containing groups may also be used as substituents of the aza-dibenzothiophene compounds and aza-dibenzofuran compounds. Such nitrogen containing groups may include carbazole, oligocarbazole, indolocarbazole, and diphenylamine. Carbazole is a nitrogen containing heteroaromatic, having high triplet energy, and has hole transporting and electron transporting properties. One advantage to using carbazole-containing compounds (i.e., carbazole, oligocarbazole and indolocarbazole) as host materials is that they simultaneously possess sufficiently large triplet energies and carrier transport properties. For example, the indolocarbazole and 3-(9-carbazolyl)carbazole have a relatively low electrochemical oxidation potential. As such, these compounds are easier to oxidize and to reverse the oxidation, which improves overall host stability. Another advantage is that these carbazole building blocks can serve as donors, while coupling with aza-dibenzothiophenes or aza-dibenzofurans which are acceptors here, to form a donor-acceptor type molecule. It is believed that these molecules having a donor-acceptor molecular arrangement contribute, at least in part, to the low voltage character in the device.

The compounds provided herein may be used as host materials in blue, green and red PHOLEDs. In particular, aza-dibenzothiophene or aza-dibenzofuran compounds substituted with triphenylene may be used in blue, green and red devices as these compounds can accommodate blue, green and red emissive dopants. Preferably, these compounds may be used in blue devices. The aza-type compounds provided herein may also be substituted with both triphenylene and nitrogen-containing substituents. These compounds substituted with both triphenylene and nitrogen-containing groups may be used in green and red devices as these compounds can accommodate green and red emissive dopants. Preferably, these compounds may be used in green devices.

The heteroaromatic compounds (i.e., aza-dibenzothiophene and aza-dibenzofuran) described herein may be more easily reduced than their dibenzothiophene or dibenzofuran counterparts, in particular by 0.2 V to 0.5 V. As a result, these aza-type compounds may provide devices having low operational voltage and long lifetimes. Without being bound by theory, it is thought that the more easily reduced compounds may provide better anion stability and easier anion injection from the electron transport layer (ETL) to the emissive layer (EML) in the device.

The compounds described herein have the formula:

X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom, and at least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom. Y is S or O. R₁ and R₂ may represent mono, di, tri, or tetra substitutions. R₁ and R₂ are independently selected from the group consisting of hydrogen, alkyl, aryl and halide. At least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ may represent mono, di, tri, or tetra or penta substitutions; and R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

The compounds described herein have the formula:

Where X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom, and at least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom. Y is S or O; wherein R₁ and R₂ may represent mono, di, tri, or tetra substitutions. R₁ and R₂ are independently selected from the group consisting of hydrogen, alkyl, aryl and halide and at least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ may represent mono, di, tri, or tetra or penta substitutions; and R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Preferably, m and n are 0, 1, 2, 3, or 4, and m+n is equal to or greater than 2 and m+n is equal to or less than 6. Without being bound by theory, it is thought that at least 2 provides better electron transport properties by providing a preferred amount of electron transport moieties. Moreover, it is thought that greater than 6 may result in an increase in sublimation temperature so that the manufacturing of devices with such compounds is not as practical.

In one aspect, at least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Specific examples of the compounds are provided, and include compounds selected from the group consisting of:

Specific examples of such compounds are provided, and include compounds selected from the group consisting of:

In another aspect, at least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Specific examples of such compounds include compounds selected from the group consisting of:

In another aspect, R₁ and R₂ are each independently selected from the group consisting of hydrogen and

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Specific examples of such compounds include compounds selected from the group consisting of:

In one aspect, at least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Specific examples of such compounds include compounds selected from the group consisting of:

In another aspect, R₁ and R₂ are each independently selected from the group consisting of hydrogen and

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Specific examples of such compounds include compounds selected from the group consisting of:

In one aspect, R₁ and R₂ are each independently selected from the group consisting of hydrogen and

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Specific examples of such compounds include compounds selected from the group consisting of:

In another aspect, R₁ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl. R₂ is hydrogen. Preferably, R′₁, R′₂, R′₃, and R′₄ are each independently hydrogen or methyl.

Specific examples of such compounds include compounds selected from the group consisting of:

A first device comprising an organic light emitting device is also provided. The device further comprises an anode, a cathode, and an organic layer disposed between the anode and the cathode. The organic layer further comprising a compound having the formula:

X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom At least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom. Y is S or O. R1 and R2 may represent mono, di, tri, or tetra substitutions. R1 and R2 are independently selected from the group consisting of hydrogen, alkyl, aryl and halide. At least one of R1 and R2 is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ may represent mono, di, tri, tetra or penta substitutions. R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl.

In one aspect, the first device is a consumer product.

Additionally, an organic light emitting device is also provided. The device comprises an anode, a cathode, and an organic emissive layer disposed between the anode and the cathode, wherein the organic layer further comprises a compound having FORMULA I. Preferably, m and n are 0, 1, 2, 3, or 4; and m+n is equal to or greater than 2 and m+n is equal to or less than 6.

In one aspect, at least one of R₁ and R₂ is selected from the group consisting of:

R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl.

In another aspect, R₁ and R₂ are each independently selected from the group consisting of hydrogen and

In one aspect, devices are provided that contain a compound selected from the group consisting of Compounds 1-93.

In particular, devices are provided wherein the compound is selected from the group consisting of Compounds 1-79.

In one aspect, the organic layer is an emissive layer and the aza-dibenzothiophene and aza-dibenzofuran having FORMULA I is a host in the organic layer. The organic layer may further comprise an emissive dopant. Preferably, the emissive dopant has the formula

where R₁ and R₂ are each independently selected from the group consisting of hydrogen, alkyl, and aryl.

As discussed above, the aza-dibenzothiophene and aza-dibenzofuran compounds having FORMULA I may be advantageously used as a host material in an emissive layer. However, these compounds may also be used as materials in an enhancement layer. In particular, the compounds described herein may be used the material in a blocking layer.

A consumer device is also provided, wherein the device further comprises an anode, a cathode and an organic layer. The organic layer further comprises an aza-dibenzothiophene or aza-dibenzofuran compound having FORMULA I.

Additionally, a process for making an aza-dibenzothiophene compound or an aza-dibenzofuran compound is provided (illustrated in FIG. 4, top). The process comprises treating an acetic acid solution of an amino-arylthio pyridine intermediate having the formula:

with ^(t)BuONO to produce an aza complex having the formula

Y is S or O. X₁ or X₂ is nitrogen. R₁ and R₂ may be a mono, di, tri, or tetra substitution. R₁ is selected from the group consisting of hydrogen, alkyl, aryl and heteroaryl; and R₂ is selected from the group consisting of hydrogen, alkyl, aryl and halide. For example, an acetic acid solution of the intermediate 3-amino-4-arylthio pyridine with halide substituents on the pyridine ring or an acetic acid solution of the intermediate 3-arylthio-4-amino pyridine with halide substituents on the pyridine ring may be treated with 1-2 eq. of ^(t)BuONO at room temperature until no gas evolved, usually around 1-3 hours.

Particular examples of the process include intermediates and aza-complexes where Y is S (i.e., dibenzothiophene intermediates and aza-dibenzothiophene complexes). Alternatively, the process may preferably include intermediates and aza-complexes where Y is O (i.e., dibenzofuran intermediates and aza-dibenzofuran complexes). The process provided herein may yield greater than 50% or greater than 70% of the aza-complexes. In particular, the yield of

may be greater than 50%.

Examples of the process to make aza-dibenzothiophene or aza-dibenzofuran compounds include intermediates where one of X₁ and X₂ is carbon and the other is nitrogen. In a particular example of the process, X₁ is nitrogen and X₂ is carbon. In another particular example, X₁ is carbon and X₂ is nitrogen.

Examples of the process to make aza-dibenzothiophene or aza-dibenzofuran compounds include compounds where R₂ includes at least one halide. In a particular example of the process, R₂ includes only halide substituents. Moreover, R₁ is preferably halide. Halide substituents may include, but are not limited to, bromide, chloride, fluoride, and iodide.

The process may also be used to make aza-dibenzothiophene or aza-dibenzofuran compounds where R₂ is not a halide (i.e. there are no further substituents on the pyridine ring). For these aza-compounds lacking a halide substituent on the pyridine ring, the amino-arylthio pyridine intermediate is treated with H₂SO₄ prior to treatment with ^(t)BuONO (illustrated in FIG. 4, bottom). For example, an acetic acid solution of the intermediate 3-amino-4-arylthio pyridine or an acetic acid solution of the intermediate 3-arylthio-4-amino pyridine may be treated with 1-5 eq. of H₂SO₄, followed by 1-2 eq. of ^(t)BuONO until no gas evolved, usually around 1-5 hours.

The materials described herein as useful for a particular layer in an organic light emitting device may be used in combination with a wide variety of other materials present in the device. For example, emissive dopants disclosed herein may be used in conjunction with a wide variety of hosts, transport layers, blocking layers, injection layers, electrodes and other layers that may be present. The materials described or referred to below are non-limiting examples of materials that may be useful in combination with the compounds disclosed herein, and one of skill in the art can readily consult the literature to identify other materials that may be useful in combination.

In addition to and/or in combination with the materials disclosed herein, many hole injection materials, hole transporting materials, host materials, dopant materials, exiton/hole blocking layer materials, electron transporting and electron injecting materials may be used in an OLED. Non-limiting examples of the materials that may be used in an OLED in combination with materials disclosed herein are listed in Table 1 below. Table 1 lists non-limiting classes of materials, non-limiting examples of compounds for each class, and references that disclose the materials.

TABLE 1 MATERIAL EXAMPLES OF MATERIAL PUBLICATIONS Hole injection materials Phthalocyanine and porphryin compounds

Appl. Phys. Lett. 69, 2160 (1996) Starburst triarylamines

J. Lumin. 72-74, 985 (1997) CF_(x) Fluorohydrocarbon polymer

Appl. Phys. Lett. 78, 673 (2001) Conducting polymers (e.g., PEDOT:PSS, polyaniline, polypthiophene)

Synth. Met. 87, 171 (1997) WO2007002683 Phosphonic acid and sliane SAMs

US20030162053 Triarylamine or polythiophene polymers with conductivity dopants

EA01725079A1

Arylamines complexed with metal oxides such as molybdenum and tungsten oxides

SID Symposium Digest, 37, 923 (2006) WO2009018009 p-type semiconducting organic complexes

US20020158242 Metal organometallic complexes

US20060240279 Cross-linkable compounds

US20080220265 Hole transporting materials Triarylamines (e.g., TPD, α-NPD)

Appl. Phys. Lett. 51, 913 (1987)

US5061569

EP650955

J. Mater. Chem. 3, 319 (1993)

Appl. Phys. Lett. 90, 183503 (2007)

Appl. Phys. Lett. 90, 183503 (2007) Triaylamine on spirofluorene core

Synth. Met. 91, 209 (1997) Arylamine carbazole compounds

Adv. Mater. 6, 677 (1994), US20080124572 Triarylamine with (di)benzothiophene/ (di)benzofuran

US20070278938, US20080106190 Indolocarbazoles

Synth. Met. 111, 421 (2000) Isoindole compounds

Chem. Mater. 15, 3148 (2003) Metal carbene complexes

US20080018221 Phosphorescent OLED host materials Red hosts Arylcarbazoles

Appl. Phys. Lett. 78, 1622 (2001) Metal 8-hydroxyquinolates (e.g., Alq₃, BAlq)

Nature 395, 151 (1998)

US20060202194

WO2005014551

WO2006072002 Metal phenoxybenzothiazole compounds

Appl. Phys. Lett. 90, 123509 (2007) Conjugated oligomers and polymers (e.g., polyfluorene)

Org. Electron. 1, 15 (2000) Aromatic fused rings

WO2009066779, WO2009066778, WO2009063833, US20090045731, US20090045730, WO2009008311, US20090008605, US20090009065 Zinc complexes

WO2009062578 Green hosts Arylcarbazoles

Appl. Phys. Lett. 78, 1622 (2001)

US20030175553

WO2001039234 Aryltriphenylene compounds

US20060280965

US20060280965

WO2009021126 Donor acceptor type molecules

WO2008056746 Aza-carbazole/DBT/DBF

JP2008074939 Polymers (e.g., PVK)

Appl. Phys. Lett. 77, 2280 (2000) Spirofluorene compounds

WO2004093207 Metal phenoxybenzooxazole compounds

WO2005089025

WO2006132173

JP200511610 Spirofluorene-carbazole compounds

JP2007254297

JP2007254297 Indolocabazoles

WO2007063796

WO2007063754 5-member ring electron deficient heterocycles (e.g., triazole, oxadiazole)

J. Appl. Phys. 90, 5048 (2001)

WO2004107822 Tetraphenylene complexes

US20050112407 Metal phenoxypyridine compounds

WO2005030900 Metal coordination complexes (e.g., Zn, Al with N{circumflex over ( )}N ligands)

US20040137268, US20040137267 Blue hosts Arylcarbazoles

Appl. Phys. Lett, 82, 2422 (2003)

US20070190359 Dibenzothiophene/ Dibenzofuran-carbazole compounds

WO2006114966, US20090167162

US20090167162

WO2009086028

US20090030202, US20090017330 Silicon aryl compounds

US20050238919

WO2009003898 Silicon/Germanium aryl compounds

EP2034538A Aryl benzoyl ester

WO2006100298 High triplet metal organometallic complex

US7154114 Phosphorescent dopants Red dopants Heavy metal porphyrins (e.g., PtOEP)

Nature 395, 151 (1998) Iridium(III) organometallic complexes

Appl. Phys. Lett. 78, 1622 (2001)

US2006835469

US2006835469

US20060202194

US20060202194

US20070087321

US20070087321

Adv. Mater. 19, 739 (2007)

WO2009100991

WO2008101842 Platinum(II) organometallic complexes

WO2003040257 Osminum(III) complexes

Chem. Mater. 17, 3532 (2005) Ruthenium(II) complexes

Adv. Mater. 17, 1059 (2005) Rhenium (I), (II), and (III) complexes

US20050244673 Green dopants Iridium(III) organometallic complexes

Inorg. Chem. 40, 1704 (2001) and its derivatives

US20020034656

US7332232

US20090108737

US20090039776

US6921915

US6687266

Chem. Mater. 16, 2480 (2004)

US20070190359

US 20060008670 JP2007123392

Adv. Mater. 16, 2003 (2004)

Angew. Chem. Int. Ed. 2006, 45, 7800

WO2009050290

US20090165846

US20080015355 Monomer for polymeric metal organometallic compounds

US7250226, US7396598 Pt(II) organometallic complexes, including polydentated ligands

Appl. Phys. Lett. 86, 153505 (2005)

Appl. Phys. Lett. 86, 153505 (2005)

Chem. Lett. 34, 592 (2005)

WO2002015645

US20060263635 Cu complexes

WO2009000673 Gold complexes

Chem. Commun. 2906 (2005) Rhenium(III) complexes

Inorg. Chem. 42, 1248 (2003) Deuterated organometallic complexes

US20030138657 Organometallic complexes with two or more metal centers

US20030152802

US7090928 Blue dopants Iridium(III) organometallic complexes

WO2002002714

WO2006009024

US20060251923

US7393599, WO2006056418, US20050260441, WO2005019373

US7534505

US7445855

US20070190359, US20080297033

US7338722

US20020134984

Angew. Chem. Int. Ed. 47, 1 (2008)

Chem. Mater. 18, 5119 (2006)

Inorg. Chem. 46, 4308 (2007)

WO2005123873

WO2005123873

WO2007004380

WO2006082742 Osmium(II) complexes

US7279704

Organometallics 23, 3745 (2004) Gold complexes

Appl. Phys. Lett. 74, 1361 (1999) Platinum(II) complexes

WO2006098120, WO2006103874 Exciton/hole blocking layer materials Bathocuprine compounds (e.g., BCP, BPhen)

Appl. Phys. Lett. 75, 4 (1999)

Appl. Phys. Lett. 79, 449 (2001) Metal 8-hydroxyquinolates (e.g., BAlq)

Appl. Phys. Lett. 81, 162 (2002) 5-member ring electron deficient heterocycles such as triazole, oxadiazole, imidaozle, benzoimidazole

Appl. Phys. Lett. 81, 162 (2002) Triphenylene compounds

US20050025993 Fluorinated aromatic compounds

Appl. Phys. Lett. 79, 156 (2001) Phenothiazine-S-oxide

WO2008132085 Electron transporting materials Anthracene- benzoimidazole compounds

WO2003060956

US20090179554 Aza triphenylene derivatives

US20090115316 Anthracene-benzothiazole compounds

Appl. Phys. Lett. 89, 063504 (2006) Metal 8-hydroxyquinolates (e.g., Alq₃, Zrq₄)

Appl. Phys. Lett. 51, 913 (1987) US7230107 Metal hydroxybenoquinolates

Chem. Lett. 5, 905 (1993) Bathocuprine compounds such as BCP, BPhen, etc

Appl. Phys. Lett. 91, 263503 (2007)

Appl. Phys. Lett. 79, 449 (2001) 5-member ring electron deficient heterocycles (e.g., triazole, oxadizaole, imidazole, benzoimidazole

Appl. Phys. Lett. 74, 865 (1999)

Appl. Phys. Lett. 55, 1489 (1989)

Jpn. J. Apply. Phys. 32, L917 (1993) Silole compounds

Org. Electron. 4, 113 (2003) Arylborane compounds

J. Am. Chem. Soc. 120, 9714 (1998) Fluorinated aromatic compounds

J. Am. Chem. Soc. 122, 1832 (2000) Fullerene (e.g., C60)

US20090101870 Triazine complexes

US20040036077 Zn (N{circumflex over ( )}N) complexes

US6528187

EXPERIMENTAL Compound Examples Example 1 Synthesis of Compound 1

Step 1.

To a 500 mL round flask was added 2-chloro-3-iodo-4-aminopyridine (10 g, 39 mmol), 4-bromothiophenol (7.0 g, 34 mmol), CuI (0.4 g, 2.0 mmol), ethylene glycol (4.9 g, 78 mmol), potassium carbonate (10.8 g, 74 mmol), and 200 mL of isopropanol. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield of 2-chloro-3-(4-bromophenylthio)-4-aminopyridine was 7.4 g.

Step 2.

To a 500 mL round flask was added 2-chloro-3-(4-bromophenylthio)-4-aminopyridine (7.0 g, 22 mmol), and 400 mL of AcOH. To this clear solution, Bu^(t)ONO (2.3 g, 22 mmol) was added drop by drop. After stirring at room temperature for 1 h, another 10 mmol of Bu^(t)ONO was added. The mixture was continued to stir for another 2 h. The reaction was quenched by water, and the product was purified by a silica gel column. Yield of 1-chloro-6-bromo-[1]Benzothieno[2,3-c]pyridine was 6.5 g.

Step 3.

To a 500 mL round flask was added 1-chloro-6-bromo-[1]Benzothieno[2,3-c]pyridine (3.6 g, 12 mmol), carbazole (6.0 g, 36 mmol), Pd₂(dba)₃ (1.1 g, 1.2 mmol), 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (S-Phos, 2.0 g, 4.8 mmol), sodium t-butoxide (6.9 g, 72 mmol), and 250 mL of xylene. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield was 4.0 g. The product was further purified by vacuum sublimation. ¹H NMR results confirmed the desired compound.

Example 2 Synthesis of Compound 2

Step 1.

To a 500 mL round flask was added 2-chloro-4-amino-5-iodo-pyridine (11.5 g, 45 mmol), 4-bromothiophenol (8.1 g, 42.8 mmol), CuI (0.4 g, 2.3 mmol), ethylene glycol (5.6 g, 90.4 mmol), potassium carbonate (12.4 g, 90.4 mmol), and 200 mL of isopropanol. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield of 2-chloro-5-(4-bromophenylthio)-4-aminopyridine was 9.2 g.

Step 2.

To a 500 mL round flask was added 2-chloro-5-(4-bromophenylthio)-4-aminopyridine (11 g, 35 mmol), and 600 mL of AcOH. To this clear solution, Bu^(t)ONO (3.6 g, 35 mmol) was added drop by drop. After stirring at room temperature for 1 hr, another 15 mmol of Bu^(t)ONO was added. The mixture was continued to stir for another 2 h. The reaction was quenched by water, and the product was purified by a silica gel column. Yield of 3-chloro-6-bromo-[1]Benzothieno[2,3-c]pyridine was 10 g.

Step 3.

To a 500 mL round flask was added 3-chloro-6-bromo-[1]Benzothieno[2,3-c]pyridine (3.0 g, 10 mmol), carbazole (4.2 g, 25 mmol), Pd(OAc)₂ (0.1 g, 0.5 mmol), P(Bu^(t))₃ (1M in toluene, 1.5 mL, 1.5 mmol), sodium t-butoxide (6.3 g, 66 mmol), and 250 mL of xylene. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield was 4.2 g. The product was further purified by vacuum sublimation. ¹H NMR results confirmed the desired compound.

Example 3 Synthesis of Compound 3

Step 1.

To a 500 mL round flask was added 2,6-dichloro-3-iodo-4-aminopyridine (7.0 g, 28.8 mmol), thiophenol (3.2 g, 34.8 mmol), CuI (0.2 g, 1.2 mmol), ethylene glycol (3.0 g, 57.6 mmol), potassium carbonate (6.6 g, 57.6 mmol), and 200 mL of isopropanol. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield of 2,6-dichloro-3-phenylthio-4-aminopyridine was 4.0 g.

Step 2.

To a 500 mL round flask was added 2,6-dichloro-3-phenylthio-4-aminopyridine (4.0 g, 14.7 mmol), and 200 mL of AcOH. To this clear solution, Bu^(t)ONO (1.5 g, 15 mmol) was added drop by drop. After stirring at room temperature for 1 h, another 8 mmol of Bu^(t)ONO was added. The mixture was continued to stir for another 2 h. The reaction was quenched by water, and the product was purified by a silica gel column. Yield of 1,3-dichloro-[1]Benzothieno[2,3-c]pyridine was 3.2 g.

Step 3.

To a 500 mL round flask was added 1,3-dichloro-[1]Benzothieno[2,3-c]pyridine (2.5 g, 10 mmol), carbazole (4.2 g, 25 mmol), Pd₂(dba)₃ (0.9 g, 1.0 mmol), 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (S-Phos, 1.6 g, 4.0 mmol), sodium t-butoxide (4.8 g, 50 mmol), and 200 mL of xylene. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield was 4.2 g. The product was further purified by vacuum sublimation. ¹H NMR results confirmed the desired compound.

Example 4 Synthesis of Compound 4

Step 1.

To a 500 mL round flask was added 1-chloro-6-bromo-[1]Benzothieno[2,3-c]pyridine (5.0 g, 16.7 mmol), carbazole (2.8 g, 16.7 mmol), Pd(OAc)₂ (0.1 g, 0.4 mmol), PBu^(t) ₃ (1.0 M solution in toluene, 1.2 mL, 1.2 mmol), sodium t-butoxide (4.8 g, 50.1 mmol), and 400 mL of xylene. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield of 1-chloro-6-(9-carbazole)-[1]Benzothieno[2,3-c]pyridine was 1.9 g.

Step 2.

To a 500 mL round flask was added 1-chloro-6-(9-carbazole)-[1]Benzothieno[2,3-c]pyridine (1.3 g, 3.4 mmol), diphenylamine (0.7 g, 4.0 mmol), Pd₂(dba)₃ (0.09 g, 0.1 mmol), 2-dicyclohexylphosphino-2′,4′,6′-triisopropylbiphenyl (0.2 g, 0.4 mmol), Pd₂(dba)₃ sodium t-butoxide (0.8 g, 8.0 mmol), and 100 mL of toulene. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield of compound 4 was 1.1 g.

Example 5 Synthesis of Compound 21

Step 1.

The solution of 2-amino-5-chloropyridine (10.0 g, 77.8 mmol) potassium acetate (7.63 g, 77.8 mmol) in 100 mL of acetic acid was heated to 85° C. and ClI (12.6 g, 77.8 mmol) in 50 mL of acetic acid was added dropwise. Reaction mixture was kept 2 h at this temperature, diluted with 1 L of water, neutralized with NaOH 1N solution to pH 7 and extracted with ethyl acetate (4×75 mL). Organic fraction were combined, washed with NaHCO₃, filtered through celite and evaporated. The residue was subjected to column chromatography on silica (eluent—hexane/ethyl acetate 1/1) providing 5-chloro-3-iodopyridin-2-amine as yellow solid (11.9 g, 60%).

Step 2.

Mixture of 5-chloro-2-methoxyphenylboronic acid (5.0 g, 26.8 mmol), 5-chloro-3-iodopyridin-2-amine (6.83 g, 26.8 mmol), sodium carbonate (8.53 g, 80.5 mmol in 50 mL of water), Pd(PPh₃)₄ (621 mg, 2 mol. %) and 100 mL of toluene was refluxed overnight under N₂. reaction mixture was cooled down to room temperature, organic layer was separated and concentrated in vacuum. The residue was subjected to column chromatography on silica gel with hexane/ethyl acetate gradient mixture as eluent, providing 3.3 g (46% yield) of 5-chloro-3-(5-chloro-2-methoxyphenyl)pyridin-2-amine.

Step 3.

Solution of 5-chloro-3-(5-chloro-2-methoxyphenyl)pyridin-2-amine (5.2 g, 19.3 mmol) in 50 mL of glacial acetic acid and 20 mL of THF was cooled down to −10° C. and tert-butyl nitrite (4.6 mL) was added dropwise. The reaction mixture was stirred overnight at 0° C., warmed to room temperature, diluted with 100 mL of water. Solid material was filtered and dried, providing 2.9 g of pure 3,6-dichlorobenzofuro[2,3-b]pyridine.

Step 4.

The mixture of 3,6-dichlorobenzofuro[2,3-b]pyridine (2.86 g, 12.01 mmol), carbazole (5.02 g, 30.003 mmol), sodium tert-butoxide (4.62 g, 48.05 mmol), 2-dicyclohexyl-phosphino-2′,6′-dimethoxybiphenyl (S-Phos, 430 mg), Pd₂(dba)₃ (910 mg) in 150 mL of dry xylenes was refluxed under N₂ for 48 h. Then reaction mixture was cooled down to room temperature, diluted with 100 mL H₂O and extracted with ethyl acetate (4×50 mL). Organic fractions were combined, dried over Na₂SO₄ anhydr, filtered and evaporated. The residual material was purified by column chromatography on silica gel (eluent—gradient mixture hexane-dichloromethane), then crystallized from hexane/dichloromethane mixture, providing target material as white tiny needles. Additional purification by sublimation (288° C. at 10⁻⁵ mm Hg) resulted 1.86 g of pure target compound.

Example 6 Synthesis of Compound 39

Step 1.

The mixture of 3-chloro-6-bromo-[1]benzothieno[2,3-c]pyridine (1.7 g, 5.8 mmol), triphenylen-2-ylboronic acid (1.6 g, 5.8 mmol), potassium phosphate tribasic (3.7 g, 17 mmol), 200 mL toluene and 10 mL water was prepared and bubbled with nitrogen for twenty minutes. Then the tris(dibenzylideneacetone)dipalladium (53 mg, 0.060 mmol) and 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (96 mg, 0.23 mmol) were added. The mixture was bubbled with nitrogen for another twenty minutes. After refluxed overnight under nitrogen, then reaction mixture was cooled to room temperature and filtered through a silica plug and washed with dichloromethane. The first several portions were discarded since they only contained impurities. The combined filtrate was concentrated to give crude product, which was recrystallized from hot dichloromethane and hexanes to give 1.8 g 3-chloro-6-(2-triphenyleneyl)-[1]Benzothieno[2,3-c]pyridine as yellow solid (4.0 mmol, 70% yield).

Step 2.

The mixture of 3-chloro-6-(2-triphenyleneyl)-[1]Benzothieno[2,3-c]pyridine (1.6 g, 3.6 mmol), carbazole (0.72 g, 4.3 mmol), Pd(OAc)₂ (20 mg, 0.090 mmol), sodium t-butoxide (1.0 g, 11 mmol), and 300 mL of xylene was prepared and bubbled with nitrogen for 15 minutes. Then PBu^(t) ₃ (1.0 M solution in toluene, 0.27 mL, 0.27 mmol) was added and the mixture was bubbled with nitrogen for another 15 minutes. After refluxed overnight, the reaction mixture was cooled to room temperature and filtered through a silica gel plug, which was then washed with dichloromethane. The xylene portion was discarded. The combined dichloromethane filtrate was concentrated and the crude product was stirred in 100 mL mixture of 20% dichloromethane in hexanes overnight. The residue was collected by filtration to give 1.7 g light yellow solid (2.9 mmol, 80% yield).

Example 7 Synthesis of Compound 59

Step 1.

The mixture of 1-chloro-6-(9-carbazole)-[1]benzothieno[2,3-c]pyridine (1.0 g, 1.6 mmol), triphenylen-2-ylboronic acid (0.85 g, 3.1 mmol), potassium phosphate tribasic (1.7 g, 7.8 mmol), 100 mL toluene and 5 mL water was prepared and bubbled with nitrogen for twenty minutes. Then the tris(dibenzylideneacetone)dipalladium (24 mg, 0.030 mmol) and 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (43 mg, 0.10 mmol) were added. The mixture was bubble with nitrogen for another twenty minutes. After refluxed overnight under nitrogen, the reaction was cooled to room temperature and concentrated. The obtained solid was redissolved in 800 mL refluxing toluene and filtered through a thin celite plug. The collected filtrate was concentrated to about 100 mL and then refluxed under nitrogen for one hour. After slowly cooled to room temperature, the precipitation was collected by filtration. The residue was stirred in 100 mL hot mixture of 20% dichloromethane in methanol and stirred overnight after it cooled to room temperature. The residue was collected by filtration and dried under vacuum to provide 1.2 g white solid (2.1 mmol, 81% yield).

Example 8 Synthesis of Compound 66

Step 1.

To a 250 mL round flask was added 2-chloro-3-iodo-4-aminopyridine (5.0 g, 19.6 mmol), thiophenol (2.16 g, 19.6 mmol), CuI (0.187 g, 0.98 mmol), ethylene glycol (2.5 g, 39 mmol), potassium carbonate (5.4 g, 39 mmol), and 150 mL of isopropanol. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield (91%) of 2-chloro-3-phenylthio-4-aminopyridine was 4.2 g.

Step 2.

To a 250 mL round flask was added 2-chloro-3-phenylthio-4-aminopyridine (2.7 g, 11.4 mmol), and 60 mL of glacial AcOH. To this clear solution, Bu^(t)ONO (1.36 g, 11.45 mmol) was added drop by drop. After stirring at room temperature for 1 h, another (1.36 g 11.45) mmol of Bu^(t)ONO was added. The mixture was continued to stir at room temperature for 18 h. The reaction was quenched by water, and the product was purified by a silica gel column. Yield (88%) of 1-chloro-benzothieno[2,3-c]pyridine was 2.2 g.

Step 3.

The mixture of 1-chloro-benzothieno[2,3-c]pyridine (1.5 g, 6.8 mmol), 3-(triphenylen-2-yl)phenylboronic acid (2.5 g, 7.2 mmol), synthesized according to U.S. Provisional Application Ser. No. 60/963,944, potassium phosphate tribasic (4.4 g, 20.4 mmol), 100 mL toluene and 10 mL water was prepared and bubbled with nitrogen for fifteen minutes. Then the tris(dibenzylideneacetone)dipalladium (63 mg, 0.068 mmol) and 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (116 mg, 0.28 mmol) were added. The mixture was bubbled with nitrogen for another twenty minutes. After refluxed overnight under nitrogen, the reaction mixture was cooled to room temperature. The product was purified by silica gel chromatography column. ˜2.7 g (81%) Compound 66 was obtained.

Example 9 Synthesis of Compound 70

Step 1.

The mixture of 1-chloro-benzothieno[2,3-c]pyridine (1.0 g, 4.5 mmol), 2-triphenylene-boronic acid (1.25 g, 4.5 mmol), synthesized according to U.S. Provisional Application Ser. No. 60/963,944, potassium phosphate tribasic (3.0 g, 18.0 mmol), 100 mL toluene and 10 mL water was prepared and bubbled with nitrogen for fifteen minutes. Then the tris(dibenzylideneacetone)dipalladium (42 mg, 0.045 mmol) and 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (77 mg, 0.18 mmol) were added. The mixture was bubbled with nitrogen for another twenty minutes. After refluxed overnight under nitrogen, the reaction mixture was cooled to room temperature. The product was purified by silical gel chromatography column. ˜1.5 g (84%) Compound 70 was obtained.

Example 10 Synthesis of Compound 71

Step 1. The solution of 2-amino-5-chloropyridine (10.0 g, 77.8 mmol) potassium acetate (7.63 g, 77.8 mmol) in 100 mL of acetic acid was heated to 85° C. and ClI (12.6 g, 77.8 mmol) in 50 mL of acetic acid was added dropwise. Reaction mixture was kept 2 h at this temperature, diluted with 1 L of water, neutralized with NaOH 1N solution to pH 7 and extracted with ethyl acetate (4×75 mL). Organic fraction were combined, washed with NaHCO₃, filtered through celite and evaporated. The residue was subjected to column chromatography on silica (eluent—hexane/ethyl acetate 1/1) providing 5-chloro-3-iodopyridin-2-amine as yellow solid (11.9 g, 60%).

Step 2. Mixture of 2-(methylthio)phenylboronic acid (5.0 g, 29.8 mmol), 5-chloro-3-iodopyridin-2-amine (7.56 g, 29.8 mmol), sodium carbonate (9.0 g, in 50 mL of water), Pd(PPh₃)₄ (621 mg) and 100 mL of toluene was refluxed overnight under N₂. reaction mixture was cooled down to room temperature, organic layer was separated and concentrated in vacuum. The residue was subjected to column chromatography on silica gel with hexane/ethyl acetate gradient mixture as eluent, providing 3.5 g of 5-chloro-3-(2-(methylthio)phenyl)pyridin-2-amine.

Step 3. Solution of 5-chloro-3-(2-(methylthio)phenyl)pyridin-2-amine (5.2 g, 19.3 mmol) in 50 mL of glacial acetic acid and 20 mL of THF was cooled down to −10° C. and tert-butyl nitrite (4.6 mL) was added dropwise. The reaction mixture was stirred overnight at 0° C., warmed to room temperature, diluted with 100 mL of water. Solid material was filtered and dried, providing 2.5 g of pure 3-chlorobenzothieno[2,3-b]pyridine.

Step 4.

The mixture of 3-chloro-[1]Benzothieno[2,3-b]pyridine (1.3 g, 5.9 mmol), 4,4,5,5-tetramethyl-2-(3-(triphenylen-2-yl)phenyl)-1,3,2-dioxaborolane (3.1 g, 7.1 mmol potassium phosphate tribasic (3.8 g, 18 mmol), 100 mL toluene and 10 mL water was prepared and bubbled with nitrogen for fifteen minutes. Then the tris(dibenzylideneacetone)dipalladium (54 mg, 0.060 mmol) and 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (97 mg, 0.24 mmol) were added. The mixture was bubbled with nitrogen for another twenty minutes. After refluxed overnight under nitrogen, the reaction mixture was cooled to room temperature and filtered to collect the precipitation. The residue was washed by methanol and then redissolved in hot toluene. The solution was filtered through a magnesium sulfate plug, which was washed with dichloromethane. The combined filtrate was concentrated to provide 700 mg white solid (1.4 mmol, 24% yield).

Example 11 Synthesis of Compound 79

Step 1.

To a 250 mL round flask was added 2-chloro-5-iodo-4-aminopyridine (5.0 g, 19.6 mmol), thiophenol (2.16 g, 19.6 mmol), CuI (0.187 g, 0.98 mmol), ethylene glycol (2.5 g, 39 mmol), potassium carbonate (5.4 g, 39 mmol), and 150 mL of isopropanol. The reaction was heated to reflux and stirred under a nitrogen atmosphere for 24 h. After cooling, the mixture was purified by a silica gel column. Yield (97%) of 2-chloro-3-phenylthio-4-aminopyridine was 4.5 g.

Step 2.

To a 250 mL round flask was added 2-chloro-3-phenylthio-4-aminopyridine (3.7 g, 16.8 mmol), and 60 mL of glacial AcOH. To this clear solution, Bu^(t)ONO (1.8 g, 16.8 mmol) was added drop by drop. After stirring at room temperature for 1 h, another (1.8 g 16.8) mmol of Bu^(t)ONO was added. The mixture was continued to stir at room temperature for 18 h. The reaction was quenched by water, and the product was purified by a silica gel column. Yield (33%) of 3-chloro-benzothieno[2,3-c]pyridine was 1.2 g.

Step 3.

The mixture of 3-chloro-benzothieno[2,3-c]pyridine (1.0 g, 4.5 mmol), 3-(triphenylen-2-yl)phenylboronic acid (2.1 g, 4.8 mmol), synthesized according to U.S. Provisional Application Ser. No. 60/963,944, potassium phosphate tribasic (2.9 g, 13.5 mmol), 100 mL toluene and 10 mL water was prepared and bubbled with nitrogen for fifteen minutes. Then the tris(dibenzylideneacetone)dipalladium (63 mg, 0.068 mmol) and 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl (116 mg, 0.28 mmol) were added. The mixture was bubbled with nitrogen for another twenty minutes. After refluxed overnight under nitrogen, the reaction mixture was cooled to room temperature. The product was purified by silica gel chromatography column. ˜1.2 g (55%) Compound 79 was obtained.

Example 12 Synthesis of Compound 80

Step 1.

Carbazole (7.3 g, 43.7 mmol), 3-bromoiodobenzene (25 g, 87.3 mmol) and sodium t-buthoxide (8.4 g, 87.3 mmol) is suspended in 150 mL of dry xylene under nitrogen atmosphere. Tris(dibenzylideneacetone)dipalladium (200 mg) and 1,1′-bis(diphenylphosphino) ferrocene (400 mg) are added as one portion and the reaction is heated to reflux and stirred under nitrogen atmosphere for 24 h. After cooling the xylene is evaporated and the residue is subjected to column chromatography on silica gel, providing 3-bromophenyl carbazole (9.5 g, yellow solidified oil).

Step 2.

3-Bromophenyl carbazole (9.5 g, 29.5 mmol), bis(pinacolato)diboron (11.2 g, 44.2 mmol), potassium acetate (8.7 g), tris(dibenzylideneacetone)dipalladium (200 mg) and 1,1′-bis(diphenylphosphino)ferrocene (400 mg) are suspended in 200 mL of dioxane and heated to reflux under nitrogen atmosphere overnight. After cooling down and evaporation the residue is subjected to column chromatography on silica gel, providing 9-(3-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)phenyl)-9H-carbazole b(6.0 g, colorless crystals).

Step 3.

1,3-Dibromobenzene (16 g, 64.9 mmol), 9-(3-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)phenyl)-9H-carbazole b(6.0 g, 11.6 mmol), potassium acetate (saturated solution of 6.6 g in water) and tetrakis(triphenylphosphine)palladium (0) (380 mg) are heated to reflux in 150 mL of toluene overnight under nitrogen atmosphere. After cooling down, evaporation and column chromatography 9-(3′-bromo-[1,1′-biphenyl]-3-yl)-9H-carbazole (5.8 g) is obtained.

Step 4.

Reaction of bis(pinacolato)diboron and 9-(3′-bromo-[1,1′-biphenyl]-3-yl)-9H-carbazole in dioxane, catalyzed with tris(dibenzylideneacetone)dipalladium and 1,1′-bis(diphenylphosphino)ferrocene with potassium acetate as base in the same conditions as Step 2 provides 9-(3′-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-[1,1′-biphenyl]-3-yl)-9H-carbazole which is purified by column chromatography on silica gel.

Step 5.

1-Chlorobenzo[4,5]thieno[2,3-c]pyridine (described as Compound 66, Step 2) and 9-(3′-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-[1,1′-biphenyl]-3-dissolved in toluene (150 mL). Catalyst (tris(dibenzylideneacetone)dipalladium, 400 mg and 2-dicyclohexylphosphino-2′,6′-dimethoxybiphenyl, 200 mg) and base (potassium phosphate tribasic) are added as one portion and reaction is heated to reflux under nitrogen atmosphere overnight. The product is purified by silica gel column, providing Compound 80.

Device Examples

All example devices were fabricated by high vacuum (<10⁻⁷ Torr) thermal evaporation. The anode electrode is 800 Å of indium tin oxide (ITO). The cathode consisted of 10 Å of LiF followed by 1000 Å of Al. All devices are encapsulated with a glass lid sealed with an epoxy resin in a nitrogen glove box (<1 ppm of H₂0 and O₂) immediately after fabrication, and a moisture getter was incorporated inside the package.

Particular devices are provided wherein P1 is the emissive dopant and an invention compound, Compound 1, Compound 2 or Compound 3, is the host. The organic stack of Device Examples 1-3 consisted of, sequentially from the ITO surface, 100 Å of P1 as the hole injecting layer (HIL), 300 Å of 4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (α-NPD) as the hole transport layer (HTL), 300 Å of the invention compound doped with 15% of P1, an Ir phosphorescent compound, as the emissive layer (EML), 100 Å of invention compound as ETL2 and 400 Å of Alq₃ (tris-8-hydroxyquinoline aluminum) as the ETL1.

Comparative Example 1 was fabricated similarly to the Device Examples, except that the EML comprised CBP as the host doped with 10% of P1, and P2 was used as the blocking layer material.

As used herein, the following compounds have the following structures:

Particular materials for use in an OLED are provided which may lead to devices having particularly good properties. The materials may be used as the host of an emissive layer or as a material in an enhancement layer. The emissive layer materials and blocking layer materials of Device Examples 1-3 are shown in Table 2. The devices were tested and the results measured are provided in Table 3. Cmpd is an abbreviation for Compound. Devices having an emissive layer and a blocking layer using Compounds 1-3 show high device efficiency, long lifetime, and reduced operating voltage.

TABLE 2 Device example Cmpd Dopant % BL 1 1 P1 15% 1 2 2 P1 15% 2 3 3 P1 15% 3 Comparative 1 CBP P1 10% P2

TABLE 3 At L = 1000 cd/m² At RT 40 mA/cm² Device CIE λmax FWHM V LE EQE PE LE per Lo LT_(80%), Gnits² example X Y (nm) (nm) (V) (cd/A) (%) lm/W EQE (cd/m²) (hr) (hr) 1 0.366 0.602 530 79 5 60.9 16.9 38.4 3.6 17,697 113 35.37 2 0.362 0.605 530 76 5.2 64.3 17.6 38.7 3.7 18,976 85 30.61 3 0.359 0.604 528 76 6 47.6 13.1 24.9 3.6 15582 106 25.81 Comparative 1 0.345 0.615 524 75 5.8 61 16.7 33 3.7 16148 83 21.64

From Device Examples 1-3, it can be seen that the Invention Compounds as hosts in green phosphorescent OLEDs give high device efficiency (i.e., LE>60 cd/A at 1000 cd/m²), indicating aza-dibenzothiophene as a chromophore has triplet energy high enough for efficient green electrophosphorescence. Also notable is the high stability of the device incorporating Compounds 1 and 2 as the host. The lifetime, T_(80%) (defined as the time required for the initial luminance, L₀, to decay to 80% of its value, at a constant current density of 40 mA/cm² at room temperature) are 113 hrs and 85 hrs for Compounds 1 and 2, respectively, with higher L₀ than the comparative example 1. This translates to a 1.5 fold improvement in the device stability. Thus, the invention compounds may function well as the enhancement layer.

Another notable feature is that Compounds 1 and 2 both gave lower device voltage, 5 V at 1000 cd/m² and 5.2 V at 1000 cd/m², respectively, compared to CBP which has 5.8 V at 1000 cd/m².

The data suggests that aza-dibenzothiophenes can be excellent hosts and enhancement layer materials for phosphorescent OLEDs, providing higher efficiency, lower voltage and an improvement in device stability multiple times better than the commonly used host, CBP.

It is understood that the various embodiments described herein are by way of example only, and are not intended to limit the scope of the invention. For example, many of the materials and structures described herein may be substituted with other materials and structures without deviating from the spirit of the invention. The present invention as claimed may therefore includes variations from the particular examples and preferred embodiments described herein, as will be apparent to one of skill in the art. It is understood that various theories as to why the invention works are not intended to be limiting. 

The invention claimed is:
 1. A compound having the formula:

wherein m and n are 0, 1, 2, 3, or 4; wherein m+n is equal to or greater than 1; wherein X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom; wherein at least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom; wherein Y is S or O; wherein R₁ and R₂ are independently selected from the group consisting of hydrogen, alkyl, aryl, and halide; and wherein at least one of R₁ and R₂ is selected from the group consisting of:

wherein R′₁, R′₂, R′₃, and R′₄ represent mono, di, tri, tetra, or no substitutions; and wherein R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl, and heteroaryl.
 2. The compound of claim 1, wherein at least one of R₁ and R₂ is:


3. The compound of claim 2, wherein m and n are 0, 1, 2, 3, or 4; and wherein m+n is equal to or greater than 2 and m+n is equal to or less than
 6. 4. The compound of claim 1, wherein the compound is selected from the group consisting of:


5. The compound of claim 1, wherein the compound is selected from the group consisting of:


6. A compound having the formula:

wherein m and n are 0, 1, 2, 3, or 4; wherein m+n is equal to or greater than 1; wherein X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom; wherein at least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom; wherein Y is S or O; wherein R₁ and R₂ are independently selected from the group consisting of hydrogen, alkyl, aryl and halide; and wherein at least one of R₁ and R₂ is selected from the group consisting of:

wherein R′₁, R′₂, R′₃, and R′₄ represent mono, di, tri, tetra or no substitutions; and wherein R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl.
 7. The compound of claim 6, wherein the compound is selected from the group consisting of:


8. A first device comprising an organic light emitting device, further comprising: an anode; a cathode; an organic layer disposed between the anode and the cathode, the organic layer further comprising a compound having the formula:

wherein m and n are 0, 1, 2, 3, or 4; wherein m+n is equal to or greater than 1; wherein X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ are independently selected from the group consisting of a carbon atom and a nitrogen atom; wherein at least one of X₁, X₂, X₃, X₄, X₅, X₆, X₇, and X₈ is a nitrogen atom; wherein Y is S or O; wherein R₁ and R₂ are independently selected from the group consisting of hydrogen, alkyl, aryl and halide; and wherein at least one of R₁ and R₂ is selected from the group consisting of:

wherein R′₁, R′₂, R′₃, and R′₄ represent mono, di, tri, tetra, or no substitutions; and wherein R′₁, R′₂, R′₃, and R′₄ are independently selected from the group consisting of hydrogen, alkyl, heteroalkyl, aryl and heteroaryl.
 9. The device of claim 8, wherein the first device is a consumer product.
 10. The device of claim 8, wherein at least one of R₁ and R₂ is


11. The device of claim 8, wherein the organic layer is an emissive layer and the compound having the formula

is a host.
 12. The device of claim 8, wherein the organic layer further comprises an emissive dopant and the emissive dopant has the formula:

wherein R₁ and R₂ of the emissive dopant are each independently selected from the group consisting of hydrogen, alkyl, and aryl. 